1. IntroductionIn modern continuous casting steelmaking, the tundish is not merely an intermediate vessel between the ladle and the mold; it is a metallurgical reactor that plays a crucial role in steel cleanliness, temperature control, and flow optimization. To achieve these objectives, a series of functional refractory products are installed in and around the tundish. These refractory items must operate under extreme conditions, including high temperature, aggressive molten steel and slag, thermal shock, erosion, and chemical corrosion.Among the most critical tundish-related refractories are the ladle shroud, stopper rod, seating block, and associated flow-control components such as tundish nozzles and sub-entry nozzles (SENs). Each of these items performs a specific function and must be designed with appropriate material composition, structure, and performance characteristics.This article provides a detailed technical overview of these key refractory products, focusing on their functions, materials, working conditions, failure mechanisms, and performance requirements.2. Ladle Shroud2.1 Function of the Ladle ShroudThe ladle shroud is a tubular refractory component installed between the ladle slide gate and the tundish impact zone. Its primary function is to protect the molten steel stream from reoxidation and nitrogen pickup during transfer from the ladle to the tundish.Key functions include:
- Creating a closed pouring system
- Preventing air aspiration and secondary oxidation
- Reducing inclusion formation
- Stabilizing the steel flow into the tundish
- Minimizing temperature loss
The ladle shroud is especially critical in the production of clean steels, such as automotive grades, IF steels, and bearing steels.2.2 Materials and StructureLadle shrouds are typically manufactured from high-purity alumina-based or zirconia-containing refractories. Common material systems include:
- Al₂O₃–C (alumina-carbon)
- Al₂O₃–ZrO₂–C
- ZrO₂–C (for high-end applications)
Key material requirements:
- High thermal shock resistance
- Excellent resistance to steel and slag corrosion
- Low wettability with molten steel
- High mechanical strength at elevated temperature
Carbon is often added to improve thermal shock resistance and reduce steel adhesion, while zirconia enhances corrosion resistance and dimensional stability.2.3 Failure MechanismsTypical failure modes of ladle shrouds include:
- Oxidation of carbon at high temperature
- Erosion by high-velocity steel stream
- Cracking due to thermal shock
- Joint leakage caused by improper gasket sealing
Advanced ladle shrouds may incorporate anti-oxidation coatings and optimized inner bore designs to extend service life.3. Stopper Rod3.1 Role of the Stopper Rod in Tundish Flow ControlThe stopper rod is a critical flow-control refractory used in tundishes equipped with stopper-controlled casting systems. By moving vertically, the stopper rod regulates the flow rate of molten steel from the tundish to the mold through the tundish nozzle.Main functions:
- Precise control of steel flow
- Stable casting speed
- Quick response during start and end of casting
- Emergency shut-off capability
Compared with slide gate systems, stopper rods offer finer flow control and are widely used in slab and bloom casting.3.2 Stopper Rod Construction and MaterialsA typical stopper rod assembly consists of:
- Stopper head (tip) – directly contacts molten steel
- Rod body – connects the head to the actuator
- Protective coatings or sleeves
Material systems for stopper heads commonly include:
- Al₂O₃–C
- Al₂O₃–ZrO₂–C
- MgO–C (for specific steel grades)
The stopper head must exhibit:
- Excellent erosion resistance
- High thermal shock resistance
- Minimal steel adhesion
- Dimensional stability during long casting sequences
The rod body is often made from dense alumina or fiber-reinforced refractories, sometimes protected by insulating sleeves.3.3 Wear and Failure IssuesCommon problems include:
- Erosion of stopper tip leading to unstable flow
- Build-up of alumina inclusions
- Cracking due to repeated thermal cycling
- Misalignment with the seating block
Advanced stopper designs optimize tip geometry and material gradients to improve service life and flow stability.4. Seating Block4.1 Function of the Seating BlockThe seating block (also known as the upper nozzle block) is installed at the bottom of the tundish and serves as the mounting interface between the tundish lining and the tundish nozzle.Its primary functions include:
- Supporting the tundish nozzle
- Ensuring precise alignment with the stopper rod
- Providing a tight seal to prevent steel leakage
- Withstanding high mechanical and thermal stresses
Although relatively small in size, the seating block is a critical safety component.4.2 Material CharacteristicsSeating blocks are typically produced from high-density, high-strength refractory materials, such as:
- Dense alumina
- Alumina-spinel composites
- Alumina–zirconia materials
Key performance requirements:
- High compressive strength
- Excellent thermal shock resistance
- Minimal deformation at casting temperature
- Good compatibility with nozzle and tundish lining materials
The bore accuracy and surface flatness of the seating block are extremely important for leak-free operation.4.3 Failure RisksPotential issues include:
- Cracking caused by thermal gradients
- Steel leakage due to poor machining tolerance
- Chemical attack from aggressive slags
- Misalignment leading to uneven stopper wear
Precision manufacturing and proper installation practices are essential to avoid these problems.5. Other Important Tundish Refractory Items5.1 Tundish NozzleThe tundish nozzle is installed below the seating block and guides molten steel into the mold or SEN. It must resist:
- Severe erosion
- Chemical attack
- Clogging by non-metallic inclusions
Common materials include Al₂O₃–C and ZrO₂–C, often with anti-clogging additives.5.2 Sub-Entry Nozzle (SEN)The SEN connects the tundish to the mold and controls steel delivery into the mold cavity. It plays a vital role in:
- Mold flow pattern control
- Slag entrainment prevention
- Surface quality improvement
Zirconia-based SENs are widely used due to their superior corrosion resistance.5.3 Impact PadInstalled in the tundish impact zone, the impact pad absorbs the kinetic energy of incoming steel from the ladle shroud, reducing lining erosion and turbulence.Materials are usually:
- High-alumina castables
- Spinel-containing refractories
5.4 Dams and WeirsThese flow-control refractories optimize steel residence time and inclusion flotation. They are usually made from insulating or alumina-based materials and are often disposable.6. Integration and System PerformanceThe performance of tundish refractories should not be evaluated individually but as a complete functional system. Proper matching of ladle shroud, stopper rod, seating block, and nozzles ensures:
- Stable casting
- Improved steel cleanliness
- Reduced breakout risk
- Lower refractory consumption
Advanced steel plants increasingly work with refractory suppliers to develop system-based solutions rather than standalone products.7. ConclusionRefractory products such as the ladle shroud, stopper rod, and seating block are indispensable components of the tundish system in continuous casting. Each item serves a distinct function, yet all must work together under extreme thermal, chemical, and mechanical conditions.With the increasing demand for clean steel, longer casting sequences, and higher productivity, the design and material selection of tundish refractories continue to evolve. Innovations in composite materials, anti-oxidation technologies, and precision manufacturing are pushing the performance of these refractory items to new levels.A deep understanding of these tundish refractories is essential for steelmakers seeking to improve casting stability, product quality, and overall operational efficiency.The difference between magnesia carbon brick and aluminum magnesia carbon brickProduction and application of isostatically pressed refractory materials